Physical Properties |
LSE-160WF |
Adhesive & Carrier |
Modified Acrylic on Conformable Acrylic Foam (closed-cell) |
Thickness |
1.60 mm |
Density |
715 kg/m³ |
Release Liner |
3M branded red siliconised polyethylene film |
Tape Colour |
White |
Performance Characteristics |
Type |
LSE-160WF |
90° Peel adhesion to Stainless Steel acc. to ASTM D3330, 90° peel angle @ RT, after 72h @ RT dwell |
54 N/cm |
90° Peel adhesion to Polypropylene acc. to ASTM D3330, 90° peel angle @ RT, after 72h @ RT dwell |
51 N/cm |
90° Peel adhesion to Glass acc. to ASTM D3330, 90° peel angle @ RT, after 72h @ RT dwell |
51 N/cm |
90° Peel adhesion to ABS acc. to ASTM D3330, 90° peel angle @ RT, after 72h @ RT dwell |
47 N/cm |
Static Shear Strength on Stainless Steel acc. to ASTM D3654, after 72h @ RT dwell (Weight held for 10.000 minutes, 3.22cm² (0.5in²), vertical test direction |
23 °C - 1000 g 70 °C – 550 g 90 °C – 250 g |
Static Shear Strength on Polypropylene acc. to ASTM D3654, after 72h @ RT dwell (Weight held for 10.000 minutes, 3.22cm² (0.5in²), vertical test direction Limited by substrate |
23 ° C - 1000 g 70 °C – 500 g 90 ° C - 500 g |
Dynamic Shear acc. to ASTM D1002 on stainless steel, after 72h @ RT dwell |
347 N /6.54cm² |
Normal Tensile (T-Block) acc. to ASTM D897 to Aluminium @ RT, after 72h @ RT dwell, test speed 50 mm/min |
290 N /6.54cm² |
Temperature Performance |
Short term (minutes, hours): 150 °C Long term (days, weeks): 90 °C |